Polyester Fabric
Nylon 6.6 DIPPED TIRE CORD FABRICS
Nylon 66 dipped tire cord fabric has the advantage of high tenacity, heat resistance, fatigue resistance, impact resistance and etc.
Dipped N66 tire cord fabric not only has the above said properties but also has the properties of good dimensional stability and high adhesion to the rubber.
Our nylon 66 dipped tire cord fabric posses excellent properties and performance. The various dipped products can be produced according to the users requirements and satisfy the world advanced level quality.
| Qualitative specification of nylon 66 Dipped fabric | |||||
| PA66 | Unit | Characteristic | |||
| 1890 D2 | 1680 D2 | 1260 D2 | 840 D2 | Denier | Yarn linear density |
| Max 2050 | No. | Total End Count | |||
| Min 310 | Min 280 | Min 210 | Min 140 | N | Breaking load |
| 22±2 | % | Elongation at break | |||
| 9.6±1 | 9.4±1 | 9.2±1 | 9.2±1 | % | Elongation at specific load of 47.7 cN/Tex |
| 4.6±1 | % | Hot air shrinkage (160ºC,2′,a 0.44 cN/Tex weight) | |||
| 320±10 | 335±10 | 390±10 | 490±10 | TPM | Twist |
| Min 190 | Min 170 | Min 150 | Min 110 | N | Adhesion ( H-test ) |
| 5±1 | % | Dip pick up | |||
| 0.81±0.06 | 0.77±0.06 | 0.66±0.06 | 0.54±0.06 | mm | Thickness |
Fabric Nylon 6
Nylon 6 DIPPED TIRE CORD FABRICS
Nylon 6 dipped tire cord fabric has the advantage of high tenacity, heat resistance, fatigue resistance, impact resistance and etc.
Dipped N6 tire cord fabric not only has the above said properties but also has the properties of good dimensional stability and high adhesion to the rubber.
Our nylon 6 dipped tire cord fabric posses excellent properties and performance. The various dipped products can be produced according to the users requirements and satisfy the world advanced level quality.
| Qualitative specification of nylon 6 Dipped fabric | |||||
| PA6 | Unit | Characteristic | |||
| 1890 D2 | 1680 D2 | 1260 D2 | 840 D2 | Denier | Yarn linear density |
| Max 2050 | No. | Total End Count | |||
| Min 310 | Min 280 | Min 210 | Min 140 | N | Breaking load |
| 22±2 | % | Elongation at break | |||
| 9.8±1 | 9.4±1 | 9.4±1 | 9.2±1 | % | Elongation at specific load of 47.7 cN/Tex |
| 7.8±1 | % | Hot air shrinkage (160ºC,2′,a 0.44 cN/Tex weight) | |||
| 320±10 | 335±10 | 390±10 | 490±10 | TPM | Twist |
| Min 190 | Min 170 | Min 150 | Min 110 | N | Adhesion ( H-test ) |
| 5±1 | % | Dip pick up | |||
| 0.81±0.06 | 0.77±0.06 | 0.66±0.06 | 0.54±0.06 | mm | Thickness |
Fabric Polyster
Polyester DIPPED TIRE CORD FABRICS
Polyester dipped tire cord fabric has the advantage of high tenacity, heat resistance, fatigue resistance, impact resistance and etc.
Dipped PET tire cord fabric not only has the above said properties but also has the properties of good dimensional stability and high adhesion to the rubber.
Our PET dipped tire cord fabric posses excellent properties and performance for radial tires. The various dipped products can be produced according to the users requirements and satisfy the world advanced level quality.
| Qualitative specification of Polyester Dipped fabric | |||||
| PET | Unit | Characteristic | |||
| 2000 D2 | 1500 D2 | 1300 D2 | 1000 D2 | Denier | Yarn linear density |
| Max 2050 | No. | Total End Count | |||
| Min 260 | Min 200 | Min 175 | Min 130 | N | Breaking load |
| 14±2 | % | Elongation at break | |||
| 3.5±1.5 | % | Elongation at specific load of 47.7 cN/Tex | |||
| 2±1 | % | Hot air shrinkage (160ºC,2′,a 0.44 cN/Tex weight) | |||
| 360±10 | 370±10 | 370±10 | 470±10 | TPM | Twist |
| Min 120 | Min 120 | Min 100 | Min 100 | N | Adhesion ( H-test ) |
| 3±1 | % | Dip pick up | |||
| 0.82±0.06 | 0.68±0.06 | 0.65±0.05 | 0.55±0.01 | mm | Thickness |
Fabric Chafer
Chafer
chafer fabric and tire cord are the essential components in tire manufacturing. This component is working as a holder in junction of curb and green tire. Although there are different technologies in tire manufacturing. There are different specifications for chafers, This Varity is in width – wrap and woof tension and even in the type of the nylon 6 and 66, made production of chafers hard.
Rubber Industries and Investment and development Co. After doing research and examination, is in the pilot production phase.
Conveyor belt
Convas for Conveyor belt
Is the structure of Convas for Conveyor belt similar to the tire cord in the tire Convas for Conveyor belt has for major parts: Canvas – upper plastic surface – down plastic surface and margin supporter. Thus Canvas is the important item in the stability of the Convas for Conveyor belt and should be resistant in front of the longitudinal and latitudinal tensions. In this case yarn materials and density of warp and woof are the important points in Canvas.
Canvases are made in different compounds and depend on the final consumption it would be selected.
Canvas NN: This kind of Canvas is produced from nylon warp and woof.
Canvas EP: This Canvas has polyester warp and nylon woof.
Canvas EE: polyester warp and woof.
Canvas PP: polypropylene warp and woof.
The last two fabrics are mostly used in form of liner.
- The number after Canvas shows the tension of Canvas in Newton per millimeter.
- Usage of the Convas for Conveyor belt is in the sand- brain sand- bog iron and Cement factories.